Application |
Product |
Features |
Min. Packing |
| 14 |
Flame Retardant - Halogenated |
CD-75P |
Brominated base Flame retardant used in latex binder, adhesive & in unsatured polysers coating. |
25 kgs |
| 15 |
Flame Retardant - Halogenated |
DE-83R (Decabromo diphenyl oxide) |
For unfilled PP: UL-94 V-0 (22~25 + 9~13% ATO) and V-2 ( 20~11 + 6~7% ATO), For filled PP (20%talc): V0 (16 ~20 + 5 ~7% ATO) & V2 : (14 ~18 + 5 ~7% ATO) |
25 kgs |
| 16 |
Flame Retardant - Halogenated |
Firemaster 2100 |
It is alternative to diephenyl oxide flame retardant and give lows cost good physical properties,high uv stability and excellent intial color. |
170kgs |
17 |
Flame Retardant - Halogenated |
PDBS-80 |
For achieving V0 in 30% glass filled Nylon: Use PDBS 80 - 22 phr, ATO - 7 phr |
25kgs |
18 |
Flame Retardant - Halogenated |
PE-68 |
Extremely effective for use in UL-94 V-0 (10~13 + 3% ATO) and V-2 ( 3~5 + 1~1.5% ATO) formulations in unfilled PP only, less loading compared to DE83R |
25 kgs |
| 19 |
Flame Retardant - Non Halogenated |
Masteret 20450 |
For achieving V0 at 8mm thickness in 25-30% glass reinforce PA66: 10 to 12% of Masteret 20450 |
25 kgs |
| 20 |
Flame Retardent - Non Halogenated |
Melagard MC |
For PA6: unreinforced, UL94 V0 use 8-12% Melagard MC, For PA6: mineral filled, UL94 V0 use 12-15%, For PA 6: glass reinforced (10-15% glass fiber), UL94 V2 use 15%, For PA66: unreinforced, UL94 V0 use 6-10%, For PA66: mineral filled, UL94 V0 use 10-14% |
15kgs |
| 21 |
Flame Retardant - Non Halogenated |
Phoslite B631C |
Effective for achiving UL94 V2 at less loading levels, dosages from 1 - 3%, compliance with rohs & WEEE directives |
10 kgs |
| 22 |
Flame Retardant - Non Halogenated |
Reofos BAPP |
Liquid phosphate ester flame retardant fo rthermoplastics in particular,styrenic blends such as PC/ABS, it offer increase resistance to stress cracking, improved agaiinst humid aging. |
230 kgs |
| 23 |
Flame Retardant - Non Halogenated |
Reofos RDP |
Reofos® RDP is a high molecular weight phosphate ester flame retardant which can impart superior flammability performance and lower volatility than is obtainable with conventional triaryl phosphates. |
230 kgs |
| 24 |
Flame Retardent Plasticizer |
Reofos 50 |
Flame retardent plasticizer for pvc in applications like conveyor belts, pvc leathercloth, cable & wiring. |
230 kgs |
25 |
Flame Retardent Plasticizer |
Reofos 65 |
Provides property/cost benefits compared to TCP, TXP or mixed alkyl-aryl phosphate esters; offer rapid fluxing in calendering compounds and good viscosity |
|
26 |
Flame Retardent Plasticizer |
Reofos 95 |
Low volatility, used as flame retardent plasticizer in PVC formulations, ideal for 'heavy metal free' pvc cables, used in combination with ATH & Ma(OH)2 |
|